Aluminum Alloy Ingot
Introduction
●It is widely applicable to new type of advanced material and special alloys in such as
Automobile
High-speed railway
Aerospace
Military industries
Power and electronic
Building material
Food and medicine packaging and so on.
●Manufacturing Process : as photo dictate
Specification
|
Product name |
Product name |
Function & Application |
Application condition |
|
Aluminium and titanium alloy Al-TI Alloy |
Al-Ti |
Refine the grain size of aluminium and aluminium alloy, and improve the mechanical property of materials |
720℃ put into molten aluminium |
|
Aluminium rare earth alloy |
Al-Re |
Improve the corrosion resistance and heat resistant strength of the alloy |
After the completion of refining, put into 730℃ molten aluminium |
|
Al-B alloy |
Al-B |
Remove the impurity element of electrical aluminium, and increase electric conductivity |
After the completion of refining, put into 750℃ molten aluminium |
|
Al-Sr alloy |
Al-Sr |
Be used for Si metamorphism and treatment of permanent mold casting, low-pressure casting or long-term casted eutectic and Improving property of castings and alloys |
After the completion of refining, put into 750℃-760℃ molten aluminium |
|
Al-Zr alloy |
Al-Zr |
Refine grains and improve high-temperature strength and weldability |
|
|
Al-Si alloy |
Al-Si |
Be used for the addition or adjustment of Si |
Be used for the elemental addition and simultaneously putting into furnace of solid materials; the elemental adjustment is put into 710-730℃ aluminium-water, and it is just needed to stir for 10 minutes |
|
Al-Mn alloy |
Al-Mn |
Be used for the addition or adjustment of Mn |
Be used for the elemental addition and simultaneously putting into furnace of solid materials; the elemental adjustment is put into 710-760℃ aluminium-water, and it is just needed to stir for 10 minutes |
|
Al-Fe alloy |
Al-Fe |
Be used for the addition or adjustment of Fe |
Be used for the elemental addition and simultaneously putting into furnace of solid materials; the elemental adjustment is put into 720-770℃ aluminium-water, and it is just needed to stir for 10 minutes |
|
Al-Cu alloy |
Al-Cu |
Be used for the addition, matching or adjustment of Cu |
Be used for the elemental addition and simultaneously putting into furnace of solid materials; the elemental adjustment is put into 710-730℃ aluminium-water, and it is just needed to stir for 10 minutes |
|
Al-Cr alloy |
Al-Cr |
Be used for the elemental addition or composition adjustment of wrought aluminium alloy |
Be used for the elemental addition and simultaneously putting into furnace of solid materials; the elemental adjustment is put into 700-720℃ aluminium-water, and it is just needed to stir for 10 minutes |
|
Al-Be alloy |
Al-Be |
Be used for the oxidation film filling and micronization in the process of aviation and spaceflight aluminium alloy production |
After the completion of refining, put into 690℃-710℃ molten aluminium |