0835 Cross-linkable Semi-conductive Outer Shielding Compound

Introduction

0835 cross-linkable semi-conductive shielding compound is used as strippable insulation shield for cross-linked polyethylene insulation power cable rated voltage up to 35KV. It’s suitable for high temperature vulcanization processing method. 0835provides excellence processability, fine surface smoothness, stable volume resistivity, low pre-cure or scorch characteristic,lower stripping force with anti-tearing property, leaving clean surface for insulation after stripped.

Advantage

●Packing: In Cardboard Box with inner PE bag, 600kg/box.

●Storage: Should be stored at room temperatures between 10~30°C. Recommended maximum storage period in dry and clean are 12 months unopened and in original packaging after the manufacture.

Specification & Parameter

Technical Parameter

Property	Test Method	Unit	Value
Density at 23°C	ASTM D 1505	g/ cm3	≤ 1.13
Tensile Strength (200 mm/min) Tensile Strength Retention (Heat Aging at 135°C after 168h)	ASTM D 638	MPA %	≥ 13 85
Elongation at Break before ageing Elongation Retention (Heat Aging at 135°C after 168h)	ASTM D 638	% %	280 85
Volume Resistivity at 20°C Volume Resistivity at 90°C	ASTM-D991	W.cm W.cm	60 ≤ 600
Hot Set Test Conditions At 200 ±2 °C x 0.2 MPa for 15 min	IEC 540-14
Elongation after loading Permanent Deformation		% %	≤ 60 ≤ 2
Moisture Content	KARL FISCHER	ppm	≤ 500
Brittleness Temperature	ASTM-D746		-40°C
Stripping Force	Q/TNYM 1-2012	N/cm	15